Sobarzo, P. A., Jessop, I. A., Pérez, Y., Hauyon, R. A., Velázquez‐Tundidor, M. V., Medina, J., González, A., García, L. E., González-Henríquez, C. M., Coll, D., Ortiz, P. A., Tundidor-Camba, A. & Terraza, C. A. (2022). Synthesis of dimethyl‐and diphenylsilane‐based oligo (azine) s: Thermal, optical, electronic, and morphological properties. Journal of Applied Polymer Science, 139(38), e52911. https://doi.org/10.1002/app.52911

Abstract: Four new oligo(azine)s were synthesized from dimethyldiphenylsilane and tetraphenylsilane core-based dialdehydes and hydrazine by high-temperature polycondesation and proposed as materials for optoelectronic applications. The oligo(azine)s were characterized by EA, FT-IR, and NMR. Although most of samples were poorly soluble, TPS-containing PAZ-4 was soluble in aprotic polar solvents. According to SEC and FT-IR studies, the samples were oligomers with up to five repeating units long. TGA showed highly stable samples with TDT_10% over 420°C except for PAZ-1 that contains a DMS core along with phenyl units, and thus, the lowest carbon content in the series. From DSC analysis, the substitution of phenyl groups in PAZ-1/3 by biphenyl moieties in PAZ-2/4 allowed to obtain oligo(azine)s with lower T_g values. PAZ-4 showed a UV-A absorption with optical band-gap values of 2.91 and 2.65 eV from UV–vis (solution) and DRS (films), respectively. PL analysis showed a violet emission. PAZ-4 showed resistivity of 29.24 Ω cm, similar to wide-band gap materials. Their contact angle measurements showed a critical surface tension of 42.29 dynes/cm, revealing its hydrophobicity. AFM analysis indicated that the PAZ-4 films had homogeneous surfaces. Young's modulus close to 4.46 GPa was established by microindentation for the PAZ-4 thin-films.